Kannada UHP Graphite Electrode Producers Furnace Electrodes Steelmaking
Imọ paramita
| Paramita | Apakan | Ẹyọ | RP 400mm (16") Data |
| Opin Opin | Electrode | mm(inch) | 400 |
| Iwọn Iwọn to pọju | mm | 409 | |
| Iwọn Iwọn Min | mm | 403 | |
| Orúkọ Gigùn | mm | 1600/1800 | |
| O pọju Gigun | mm | Ọdun 1700/1900 | |
| Min Gigun | mm | 1500/1700 | |
| Iwọn iwuwo lọwọlọwọ | KA/cm2 | 14-18 | |
| Agbara Gbigbe lọwọlọwọ | A | 18000-23500 | |
| Specific Resistance | Electrode | μΩm | 7.5-8.5 |
| ori omu | 5.8-6.5 | ||
| Agbara Flexural | Electrode | Mpa | ≥8.5 |
| ori omu | ≥16.0 | ||
| Modulu odo | Electrode | Gpa | ≤9.3 |
| ori omu | ≤13.0 | ||
| Olopobobo iwuwo | Electrode | g/cm3 | 1.55-1.64 |
| ori omu | ≥1.74 | ||
| CTE | Electrode | ×10-6/℃ | ≤2.4 |
| ori omu | ≤2.0 | ||
| Eeru akoonu | Electrode | % | ≤0.3 |
| ori omu | ≤0.3 |
AKIYESI: Eyikeyi ibeere kan pato lori iwọn le jẹ funni.
RP Graphite Electrode Agbekale
Agbara deede (RP) elekiturodi lẹẹdi ni a ṣe nipasẹ iṣelọpọ ite epo epo coke lasan, awọn ibeere ohun elo aise ko ni didara ga, iwọn otutu graphitization jẹ kekere, nitorinaa RP grade graphite electrode's resistivity jẹ giga, resistance mọnamọna gbona ko dara, alasọdipúpọ laini jẹ nla, lọwọlọwọ gbigba laaye jẹ kekere, o dara fun ṣiṣe irin lasan. RP graphite elekiturodu jẹ diẹ dara fun wọpọ agbara arc ileru ti 300Kv.A/t fun ton ileru yo.
RP Graphite Electrode Lọwọlọwọ Gbigbe Agbara
| Opin Opin | Agbara deede(RP) Electrode Graphite | ||
| mm | Inṣi | Agbara Gbigbe lọwọlọwọ(A) | Ìwúwo lọwọlọwọ (A/cm2) |
| 300 | 12 | 10000-13000 | 14-18 |
| 350 | 14 | 13500-18000 | 14-18 |
| 400 | 16 | 18000-23500 | 14-18 |
| 450 | 18 | 22000-27000 | 13-17 |
| 500 | 20 | 25000-32000 | 13-16 |
| 550 | 22 | 28000-36000 | 12-15 |
| 600 | 24 | 30000-36000 | 11-13 |
Onibara itelorun Guarantee
“Ijagun-Iduro Kan” rẹ fun GRAPHITE ELECTRODE ni idiyele ti o kere julọ ti iṣeduro
Lati akoko ti o kan si Gufan, ẹgbẹ awọn amoye wa ti pinnu lati pese iṣẹ to dayato, awọn ọja didara, ati ifijiṣẹ akoko, ati pe a duro lẹhin gbogbo ọja ti a ṣe.
Awọn ọja ti o jọmọ
-
UHP 700mm Graphite Electrode Large Dimeter Gra...
Paramita Imọ-ẹrọ Apakan Apakan UHP 700mm(28”) Data Iwọn Iwọn Electrode mm(inch) 700 Max Diamita mm 714 Min Diamita mm 710 Iforukọ Gigun mm 2200/2700 Max Gigun mm 2300/2800 Max Gigun mm 2300ns KA/2800 Min Gigun mm210n / cm2 18-24 Agbara Gbigbe lọwọlọwọ A 73000-96000 Specific Resistance Electrode μΩm 4.5-5.4 ori ọmu 3.0-3.6 Flexu...
-
Electrode Graphite Nlo Fun Isọdọtun Corundum E...
Chart Paramita Imọ-ẹrọ 1: Paramita Imọ-ẹrọ Fun Iwọn Iwọn Iwọn Kekere Electrode Dimeter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.0 ≥9.5 . 1.55-1.64 ≤2.4 ≤0.3 ori omu 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.3 ≤2.4 ≤0.3 Nip...
-
Ultra High Power UHP 650mm Furnace Graphite Ele ...
Paramita Imọ-ẹrọ Apakan Apakan UHP 650mm(26”) Data Iwọn Iwọn Electrode mm(inch) 650 Max Diamita mm 663 Min Diamita mm 659 Iforukọ Gigun mm 2200/2700 Max Gigun mm 2300/2800 Max Gigun mm 2300ns KA/2800 Min Gigun mm210n / cm2 21-25 Agbara Gbigbe lọwọlọwọ A 70000-86000 Specific Resistance Electrode μΩm 4.5-5.4 ori ọmu 3.0-3.6 Flexu...
-
Iwọn Iwọn Kekere 225mm Furnace Graphite Electrode...
Chart Paramita Imọ-ẹrọ 1: Paramita Imọ-ẹrọ Fun Iwọn Iwọn Iwọn Kekere Electrode Dimeter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.0 ≥9.5 . 1.55-1.64 ≤2.4 ≤0.3 ori omu 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.3 ≤2.4 ≤0.3 Nip...
-
Ina Arc Furnace Graphite Electrodes HP550m...
Imọ paramita Apakan Apakan HP 550mm(22”) Data Nominal Diamita Electrode mm(inch) 550 Max Diamita mm 562 Min Diamita mm 556 Nominal Length mm 1800/2400 Max Gigun mm 1900/2500/1900/2500 Min Gigun mm 130ns Current cm2 14-22 Agbara Gbigbe lọwọlọwọ A 34000-53000 Specific Resistance Electrode μΩm 5.2-6.5 ori ọmu 3.2-4.3 Flexural S...
-
Giga iwuwo Kekere Ileru ileru Graphite El...
Chart Paramita Imọ-ẹrọ 1: Paramita Imọ-ẹrọ Fun Iwọn Iwọn Iwọn Kekere Electrode Dimeter Part Resistance Flexural Strength Young Modulus Density CTE Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.0 ≥9.5 . 1.55-1.64 ≤2.4 ≤0.3 ori omu 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.3 ≤2.4 ≤0.3 Nip...